Description
ADHESIVES RE 400/PLUS
Universal acrylic adhesive in water dispersion for laying floors
resilient on absorbent or semi-absorbent substrates
¤Description
ADESIVER RE 400/PLUS is an adhesive in water dispersion
based on acrylic terpolymers characterized by a very high
dry residue, excellent spreadability, low water content.
Specific for indoor installation of:
- carpet and needle punched with any reverse as long as
dimensionally stable;
- linoleum up to 3 mm thick;
- vinyl floors supported by felt;
- PVC flooring in rolls or squares;
- textile floors;
- semi-rigid vinyls.
¤Features
Single component cure ratio
Creamy look
Ivory white colour
Application temperature +10°C ÷ +25°C
No. 1-3 notched trowel application
Waiting time 5-15 minutes (1)
Maximum open time 20 minutes (1)
Walkability time after about 2-4 hours (1)
Commissioning after approx. 24-48 hours (1)
Yield 250-350 g/m² depending on
background.
Possible water dilution
Storage stability 2 years (2)
Packages 5-12-20 Kg
Cleaning tools water (with fresh adhesive)
1 at 20°C and 65% RH
2 in closed original containers and at temperatures between +10°C and +25°C
¤Laying conditions
◊ Background
dry, healthy, non-dusting and not overly rough.
◊ Substrate humidity
2.0% max for cement substrates
1.7% max for cement substrates with heating
radiant
0.5% max for anhydrite substrates
0.2% max for anhydrite substrates with heating
radiant
¤How to use
It is essential to ensure that there is no rising damp
from the background.
Clean the substrate to be treated, completely eliminating the
traces of oil, grease, wax or paint stains.
Dry but dusty substrates must be primed
with PRYMER W, PRYMER SF 1105, PRYMER PUB 77 or
CHIMIGRIP suitably diluted (see relevant technical data sheets)
and subsequently shaved with the products of the RASOCHIM line
(see related technical sheets).
Cement substrates with too high residual humidity
should be primed with: PRYMER EPOX WETT, PRYMER WB 328
S, PRYMER SF 1105 and PRYMER PUB 77 (see relative sheets
techniques), sandblasted and subsequently shaved with the products of
RASOCHIM line (see relative technical sheets).
Semi-absorbent or non-absorbent substrates must be
always shaved with the products of the RASOCHIM line (see
relative technical data sheets), after preparation of the surface
with CHIMIGRIP as an adhesion promoter (see relevant sheet
technique).
Do not lay on substrates that are not insulated from any rising damp
humidity (crawl spaces without vapor barrier, damp walls, etc...)
Laying on suitable substrates
Apply the adhesive to the substrate using the appropriate spatula
toothed, working it in order to incorporate any powder
residual.
Wait for the adhesive to flash off (at least 5 minutes) e
proceed with the drafting of the squares or sheets. After
final positioning exercise on the entire surface a
even pressure to ensure complete contact
of the adhering with the glue and to favor the elimination of
any air pockets.
Notes: always remove the coverings to be glued from the packaging
a few hours before laying in order to release tension
and homologate them to the environmental climatic conditions. Possible
time variations are attributable to different absorptions
of the background.
Some tires may be polluted by substances
release agents or paraffins. A cleaning is therefore recommended
preventive with ACETONE THINNER.
¤Warnings
Protect from frost both during transport and storage.
Avoid prolonged exposure to temperatures below 0°C.
Storage temperatures above +25°C reduce the storage time
storage stability.